There are two main methods for manufacturing PCBN blades: one is a one-time polymerization, that is, directly using hexagonal boron nitride (HBN) to polymerize into a high-density sintered body. The other is a secondary polymerization method. This method first synthesizes high-density cubic boron nitride (CBN), and then uses high temperature and high pressure as a raw material to form polycrystalline cubic boron nitride. At present, secondary polymerization methods with added binders are more common:
1. Añadir la sinterización CBN del encuadernador metálico
Hay muchos tipos de aglutinantes metálicos, principalmente Ni, Co, Ti, ti-al, etc. A la temperatura de sinterización, el aglutinante metálico se convierte en la fase líquida. La aparición de la fase líquida tiene un cierto efecto de promoción en la sinterización de CBN, y la sinterización puede llevarse a cabo a una temperatura y presión ligeramente más bajas. Además, como el CBN es insoluble en el aglutinante metálico, el proceso de disolución y precipitación que puede promover la contracción y el crecimiento del cristal no se producirá. Durante el proceso de sinterización, el cobalto en el carburo cementado penetra en el límite del grano CBN en estado líquido, y el carburo cementado está estrechamente unido al cuerpo sinterizado de CBN. La dureza de la herramienta PCBN con un aglutinante metálico es menor que la de la herramienta sinterizada CBN pura, pero su resistencia es buena. Marcas como el AMB90 del Elemento Seis, el BZN6000 de GE y el MB710 de Mitsubishi están todas hechas del encuadernador de metal sinterizado.
2. La adición de un encuadernador cerámico de sinterización CBN
Ceramic binder mainly includes TiN, TiC, Al2O3, etc. Crack due to sintering process, so much in the vitrified bond of iron group elements (iron, cobalt, nickel) and Mo or Mo2C increase strength between ceramic ion, have the effect of the medium of fluid transmitting pressure, is conducive to form internal sintered body without deformation, such as molybdenum can also improve the wettability between ceramic particles and iron. Ceramic binder PCBN binder content is generally higher, toughness than metal binder tool is poor, but its high-temperature resistance performance is better. Such products include DBA80 and DBC50 of British Element six company, BZN7000S and BZN8200 of American GE company, and NBX300 and NBX3200 of Sumitomo Japan.
3. Sinterización pura CBN
El nitruda de boro cúbico policristalino también se puede formar mediante un método de sinterización directa para que un aglutinante no se utilice en el policristal CBN. La recristalización y el crecimiento de granos ocurren durante la sinterización de CBN. Los granos de CBN policristalina después de la sinterización no son el único CBN original - partículas de cristal. Este tipo de herramienta PCBN tiene una buena resistencia al desgaste y una larga vida útil, pero es difícil hacer la cuchilla con alta resistencia y gran tamaño debido a su fragilidad y a las duras condiciones de temperatura.