CBN (Cubic Boron Nitride) was first synthesized in the 1950s by American general electric (GE) under high temperature and high pressure by the artificial methods. Its hardness reaches HV8000, which is second only to diamond (HV10000) and much higher than other materials. It and diamond are collectively known as superhard materials.
El cristal CBN y el cristal de diamante pertenecen al tipo de esfalerita, y la constante de red es similar, el tipo de enlace químico es el mismo, por lo que CBN tiene la dureza y resistencia a la compresión cerca del diamante, y debido a que está compuesto de átomos de N, B, tiene mayor estabilidad térmica e inercia química que el diamante.
The manufacturing method of CBN tool material is mainly the hot pressing method. The original material of pressing CBN single crystal powder — hexagonal boron nitrous oxide powder (HBN) is placed in the chamber of leaf wax, and the catalyst is added. With a hydraulic press with six or two heads, the CBN single crystal powder is formed under 1600℃ and 5 ~ 6GPa under 10min of hot pressing. Single crystal powder can be used in abrasives and abrasives. With the CBN single crystal powder plus catalyst and binder, at 1800℃, 5 ~ 6GPa under the pressure of 3 minutes can be obtained PCBN overall blade or composite blade (cemented carbide backing, there is 0.5mm left and right CBN thin layer).
La rectificadora de herramientas Demina puede moler las herramientas CBN con alta calidad.